Steel Shots
This type of abrasive is a globular product, made of hypereutectoid steel. It corresponds with the international standards and undergoes a fully controlled thermal treatment in the conditions of achieving the optimal resilience and fatigue capacity of the metal. Steel shot is used to achieve the bulk and the maximum kick effect and is mostly applied for shot-casting and shot-blasting of castings, forgings and rolled products, for surface hardening of the machine building parts, for rolls’ ragging and for other technological purposes.
| Dimension mm |
Hardness HV, HRC |
Density kg/m3 |
Components content, % | ||||
| Carbon | Silicon | Manganese | Sulphur | Phosporus | |||
|
S70; S110; S170;
S230; S330; S390; S460; S550 S660; S780 S930; S1100; S1320 |
40-50 HRc | min 7200 | 0,8 – 1,2 | min 0,4 | 0,35 – 1,2 | max 0,05 | max 0,05 |
This type of abrasive is a globular product, made of hypereutectoid steel. It corresponds with the international standards and undergoes a fully controlled thermal treatment in the conditions of achieving the optimal resilience and fatigue capacity of the metal. Steel shot is used to achieve the bulk and the maximum kick effect and is mostly applied for shot-casting and shot-blasting of castings, forgings and rolled products, for surface hardening of the machine building parts, for rolls’ ragging and for other technological purposes.
| Dimension mm |
Hardness HRC |
Density kg/m3 |
Components content, % | ||||
| Carbon | Silicon | Manganese | Sulphur | Phosporus | |||
|
S70; S110; S170;
S230; S330; S390; S460; S550 S660; S780 S930; S1100; S1320 |
40-50HRc | min 7200 | 0,8 – 1,2 | min 0,4 | 0,35 – 1,2 | max 0,05 | max 0,05 |